Methods for depositing tungsten layers employing atomic layer deposition techniques

ABSTRACT

In one embodiment of the invention, a method for forming a tungsten-containing layer on a substrate is provided which includes positioning a substrate containing a barrier layer disposed thereon in a process chamber, exposing the substrate to a first soak process for a first time period and depositing a nucleation layer on the barrier layer by flowing a tungsten-containing precursor and a reductant into the process chamber. The method further includes exposing the nucleation layer to a second soak process for a second time period and depositing a bulk layer on the nucleation layer. In one example, the barrier layer contains titanium nitride, the first and second soak processes independently comprise at least one reducing gas selected from the group consisting of hydrogen, silane, disilane, dichlorosilane, borane, diborane, derivatives thereof and combinations thereof and the nucleation layer may be deposited by an atomic layer deposition process or a pulsed chemical vapor deposition process while the bulk layer may be deposited by a chemical vapor deposition process or a physical vapor deposition process.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 11/038,592, entitled “Methods for Depositing Tungsten Layers Employing Atomic Layer Deposition Techniques,” filed on Jan. 19, 2005 now U.S. Pat. No. 7,405,158, which is a continuation-in-part of U.S. patent application Ser. No. 10/418,728, entitled “Method for Depositing Refractory Metal Layers Employing Sequential Deposition Techniques,” filed on Apr. 18, 2003 now abandoned, which is a continuation-in-part of application Ser. No. 10/268,195, now U.S. Pat. No. 6,797,340, filed Oct. 10, 2002, which claims priority to U.S. Provisional Patent Application Ser. No. 60/328,451, entitled “Method and Apparatus for Depositing Refractory Metal Layers Employing Sequential Deposition Techniques,” filed on Oct. 10, 2001, which are all hereby incorporated by reference in their entirety, which U.S. patent application Ser. No. 11/038,592 is also a continuation-in-part of U.S. patent application Ser. No. 10/879,448, entitled, “Method for Depositing Refractory Metal Layers Employing Sequential Deposition Techniques,” filed Jun. 29, 2004 now abandon, which is a continuation of U.S. Pat. No. 6,797,340, filed Oct. 10, 2002, which claims priority to U.S. Provisional Patent Application Ser. No. 60/328,451, entitled “Method and Apparatus for Depositing Refractory Metal Layers Employing Sequential Deposition Techniques,” filed on Oct. 10, 2001, which are all hereby incorporated by reference in their entirety, which U.S. patent application Ser. No. 11/038,592 is also a continuation-in-part of U.S. patent application Ser. No. 10/762,764, entitled “Method and Apparatus for Depositing Refractory Metal Layers Employing Sequential Deposition Techniques to form Nucleation Layer,” filed on Jan. 22, 2004 now abandon, which is a continuation of U.S. patent application Ser. No. 09/678,266, entitled “Method and Apparatus for Depositing Refractory Metal Layers Employing Sequential Deposition Techniques to Form Nucleation Layer,” filed on Oct. 3, 2000, and issued as U.S. Pat. No. 7,101,795, which is a continuation-in-part of application Ser. No. 09/605,593, now U.S. Pat. No. 6,551,929, filed on Jun. 28, 2000, which are all hereby incorporated by reference in their entirety, and which U.S. patent application Ser. No. 11/038,592 is also a continuation-in-part of U.S. patent application Ser. No. 10/196,514, entitled “Method and Apparatus for Depositing Tungsten After Surface Treatment to Improve Film Characteristics,” filed on Jul. 15, 2002, and issued as U.S. Pat. No. 6,936,538, which claims priority to U.S. Provisional Patent Application Ser. No. 60/305,765, entitled “Method and Apparatus for Depositing Tungsten After Surface Treatment to Improve Film Characteristics,” filed on Jul. 16, 2001, which are both hereby incorporated by reference in their entirety.

BACKGROUND OF THE INVENTION

1. Field of the Invention

Embodiments of the invention relate to the processing of semiconductor substrates. More particularly, embodiments of the invention relate to deposition of tungsten layers on semiconductor substrates using vapor deposition techniques.

2. Description of the Related Art

The semiconductor processing industry continues to strive for larger production yields while increasing the uniformity of layers deposited on substrates having larger surface areas. These same factors in combination with new materials also provide higher integration of circuits per unit area of the substrate. As circuit integration increases, the need for greater uniformity and process control regarding layer thickness rises. As a result, various technologies have been developed to deposit layers on substrates in a cost-effective manner, while maintaining control over the characteristics of the layer.

Chemical vapor deposition (CVD) is one of the most common deposition processes employed for depositing layers on a substrate. CVD is a flux-dependent deposition technique that requires precise control of the substrate temperature and the precursors introduced into the processing chamber in order to produce a desired layer of uniform thickness. These requirements become more critical as substrate size increases, creating a need for more complexity in chamber design and gas flow technique to maintain adequate uniformity.

A variant of CVD that demonstrates excellent step coverage is cyclical deposition or atomic layer deposition (ALD). Cyclical deposition is based upon atomic layer epitaxy (ALE) and employs chemisorption techniques to deliver precursor molecules on a substrate surface in sequential cycles. The cycle exposes the substrate surface to a first precursor, a purge gas, a second precursor and the purge gas. The first and second precursors react to form a product compound as a film on the substrate surface. The cycle is repeated to form the layer to a desired thickness.

Formation of film layers at a high deposition rate while providing adequate step coverage are conflicting characteristics often necessitating the sacrifice of one to obtain the other. This conflict is true particularly when refractory metal layers are deposited over gaps or vias during the formation of contacts interconnecting adjacent metallic layers separated by dielectric layers. Historically, CVD techniques have been employed to deposit conductive material such as refractory metals in order to inexpensively and quickly form contacts. Due to the increasing integration of semiconductor circuitry, tungsten has been used based upon superior step coverage. As a result, deposition of tungsten employing CVD techniques enjoys wide application in semiconductor processing due to the high throughput of the process.

Depositing tungsten by conventional CVD methods, however, is attendant with several disadvantages. For example, ALD processes deposit tungsten films into vias containing high aspect ratios (e.g., 20), whereas conventional CVD processes will usually cause similar vias to “pinch-off” and not completely fill. Also, blanket deposition of a tungsten layer on a semiconductor wafer is time-consuming at temperatures below 400° C. The deposition rate of tungsten may be improved by increasing the deposition temperature to, for example, about 500° C. to about 550° C. However, temperatures in this higher range may compromise the structural and operational integrity of the underlying portions of the integrated circuit being formed. Use of tungsten has also frustrated photolithography steps during the manufacturing process as it results in a relatively rough surface having a reflectivity of 70% or less than that of silicon (thickness and wavelength dependent). Further, tungsten has proven difficult to deposit uniformly. Poor surface uniformity typically increases film resistivity.

Therefore, there is a need for an improved technique to deposit conductive layers with good uniformity using cyclical deposition techniques.

SUMMARY OF THE INVENTION

In one embodiment of the invention, a method for forming a tungsten-containing layer on a substrate is provided which includes positioning a substrate containing a barrier layer disposed thereon in a process chamber, exposing the substrate to a first soak process for a first time period and depositing a nucleation layer on the barrier layer by flowing a tungsten-containing precursor and a reductant into the process chamber. The method further includes exposing the nucleation layer to a second soak process for a second time period and depositing a bulk layer on the nucleation layer. In one example, the barrier layer contains titanium nitride, the first and second soak processes independently comprise at least one reducing gas selected from the group consisting of hydrogen, silane, disilane, dichlorosilane, borane, diborane, derivatives thereof and combinations thereof and the nucleation layer may be deposited by an atomic layer deposition process or a pulsed chemical vapor deposition process while the bulk layer may be deposited by a chemical vapor deposition process or a physical vapor deposition process.

In another example of the invention, a method for forming a tungsten-containing layer on a substrate is provided which includes positioning a substrate containing a barrier layer disposed thereon in a process chamber and exposing the substrate to a first reductant to form a first treated surface on the barrier layer. The method further includes depositing a nucleation layer on the treated surface by a vapor deposition process, exposing the substrate to a second reductant to form a second treated surface, and depositing a bulk layer on the second treated surface.

In another example of the invention, a method for forming a tungsten-containing layer on a substrate is provided which includes positioning a substrate in a process chamber, depositing a nucleation layer on the substrate by a vapor deposition process, exposing the nucleation layer to a second soak process to form a treated surface, and depositing a bulk layer on the second treated surface.

In another example of the invention, a method for forming a tungsten-containing layer on a substrate is provided which includes positioning a substrate containing a barrier layer disposed thereon in a process chamber, exposing the substrate to a first soak process and depositing a nucleation layer on the barrier layer by a pulsed chemical vapor deposition process or an atomic layer deposition process. The method further includes exposing the nucleation layer to a second soak process and depositing a bulk layer on the nucleation layer by a chemical vapor deposition process or a physical vapor deposition process.

BRIEF DESCRIPTION OF THE DRAWINGS

So that the manner in which the above recited features of the invention can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of the invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.

FIG. 1 illustrates a process sequence for the formation of a tungsten layer using a cyclical deposition technique according to one embodiment described herein;

FIG. 2 illustrates a process sequence for the forming of a tungsten-containing material according to one embodiment described herein;

FIG. 3A shows an exemplary integrated processing platform;

FIG. 3B shows another exemplary integrated processing platform;

FIGS. 4A-4C show cross sectional views of a via, a nucleated via and a filled via;

FIG. 5 shows a cross sectional view of an exemplary metal oxide gate device formed according to an embodiment of the invention; and

FIG. 6 shows a cross sectional view of a conventional DRAM device formed according to an embodiment of the invention.

DETAILED DESCRIPTION OF THE INVENTION

Embodiments of the invention provide an improved process for depositing tungsten-containing films. The process utilizes soak processes and vapor deposition processes, such as an atomic layer deposition (ALD) or pulsed-CVD to provide tungsten films having significantly improved surface uniformity and production level throughput. In one aspect, the process includes at least one soak process prior to tungsten deposition to activate the underlying surface on the substrate. Preferably, the underlying surface is exposed to a reductant, such as diborane (B₂H₆) or silane (SiH₄), although it is believed that other reductant will achieve similar results. In general, the soak process may occur in-situ for a period of time in a range from about 1 second to about 90 seconds at similar processing conditions as a subsequent tungsten deposition process, thereby significantly increasing production throughput. For example, a soak process may be conducted to the barrier layer prior to depositing a nucleation layer thereon and/or a soak process may be conducted to the nucleation layer prior to depositing a bulk layer thereon.

A “substrate surface”, as used herein, refers to any substrate or material surface formed on a substrate upon which film processing is performed. For example, a substrate surface on which processing can be performed include materials such as silicon, silicon oxide, silicon nitride, doped silicon, germanium, gallium arsenide, glass, sapphire, and any other materials such as metals, metal nitrides, metal alloys, and other conductive materials, depending on the application. Barrier layers, metals or metal nitrides on a substrate surface include titanium, titanium nitride, tungsten nitride, tantalum and tantalum nitride. A substrate surface may also include dielectric materials such as silicon dioxide and carbon doped silicon oxides. Substrates may have various dimensions, such as 200 mm or 300 mm diameter wafers, as well as, rectangular or square panes.

“Atomic layer deposition” or “cyclical deposition” as used herein refers to the sequential introduction of two or more reactive compounds to deposit a layer of material on a substrate surface. The two or more reactive compounds are alternatively introduced into a reaction zone of a processing chamber. Each reactive compound is separated by a time delay to allow each compound to adhere and/or react on the substrate surface. In one aspect, a first precursor or compound A is pulsed into the reaction zone followed by a first time delay. Next, a second precursor or compound B is pulsed into the reaction zone followed by a second delay. During each time delay a purge gas, such as argon, is introduced into the processing chamber to purge the reaction zone or otherwise remove any residual reactive compound or by-products from the reaction zone. Alternatively, the purge gas may flow continuously throughout the deposition process so that only the purge gas flows during the time delay between pulses of reactive compounds. The reactive compounds are alternatively pulsed until a desired film or film thickness is formed on the substrate surface. In either scenario, the ALD process of pulsing compound A, purge gas, compound B and purge gas is a cycle. A cycle can start with either compound A or compound B and continue the respective order of the cycle until achieving a film with the desired thickness.

FIG. 1 illustrates an exemplary process sequence 100 for forming an improved tungsten-containing film according to one embodiment of the invention. A substrate to be processed is first loaded into a process chamber capable of performing cyclical deposition and the process conditions are adjusted (step 110). The substrate is then exposed to a soak process lasting in a range from about 1 second to about 90 seconds (step 120). A pulse of a tungsten-containing precursor accompanied with a suitable carrier gas is introduced into the processing chamber (step 130). A pulse of gas is then pulsed into the process chamber (step 140) to purge or otherwise remove any residual tungsten-containing precursor or by-products. Next, a pulse of a reductant or reducing compound accompanied with a suitable carrier gas is introduced into the process chamber (step 150). The reducing gas may be the same compound as the gas used for the soak process (step 120) or alternatively, the reducing gas may be a different compound, depending on the product throughput requirements and the device applications. A pulse of purge gas is then introduced into the processing chamber (step 160) to purge or otherwise remove any residual reducing compound.

Suitable carrier gases or purge gases include helium, argon, nitrogen, hydrogen, forming gas and combinations thereof. Typically, the borane compounds utilize argon or nitrogen as a carrier gas and the silane compounds use hydrogen, argon or nitrogen as the carrier gas.

A “pulse” as used herein is intended to refer to a quantity of a particular compound that is intermittently or non-continuously introduced into a reaction zone of a processing chamber. The quantity of a particular compound within each pulse may vary over time, depending on the duration of the pulse. The duration of each pulse is variable depending upon a number of factors such as, for example, the volume capacity of the process chamber employed, the vacuum system coupled thereto, and the volatility/reactivity of the particular compound itself.

Referring to step 170, after each deposition cycle (steps 130 through 160), a tungsten nucleation layer having a particular thickness will be deposited on the substrate surface. Usually, each deposition cycle forms a layer with a thickness in the range from about 1 Å to about 10 Å. Depending on specific device requirements, subsequent deposition cycles may be needed to deposit tungsten nucleation layer having a desired thickness. As such, a deposition cycle (steps 130 through 160) can be repeated until the desired thickness for the tungsten film is achieved. The nucleation layer is typically deposited to a thickness in a range from about 10 Å to about 200 Å. Thereafter, the process is stopped as indicated by step 180 when the desired thickness is achieved.

Suitable tungsten-containing precursors or compounds include tungsten hexafluoride (WF₆), tungsten hexachloride (WCl₆), tungsten carbonyl (W(CO)₆), bis(cyclopentadienyl)tungsten dichloride (Cp₂WCl₂) and mesitylene tungsten tricarbonyl (C₉H₁₂W(CO)₃), as well as derivatives thereof. Suitable reducing compounds and soak compounds include silane compounds, borane compounds, phosphine compounds, ammonia and ammine compounds and hydrogen. Silane compounds include silane, disilane, trisilane, tetrasilane, chlorosilane, dichlorosilane, tetrachlorosilane, hexachlorodisilane and derivatives thereof, while borane compounds include borane, diborane, triborane, tetraborane, pentaborane, alkylboranes, such as triethylborane and derivatives thereof. The preferred reducing compounds and reductant for the soak process include silane, disilane, diborane, hydrogen and combinations thereof.

The substrate surface generally contains a barrier layer disposed thereon. The tungsten nucleation layer is deposited on the barrier layers. The substrate surface is exposed to a soak process at a temperature in the range from about 100° C. to about 600° C., preferably in the range from about 100° C. to about 500° C., more preferably in the range from about 300° C. to about 450° C. In one example, the temperature of the soak process is maintained for the subsequent vapor deposition process. The soak process (step 120) is typically performed with the process chamber at a pressure in the range from about 1 Torr to about 150 Torr, preferably in the range from about 5 Torr to about 90 Torr. In some examples, a pressure is in a range from about 5 Torr to about 20 Torr. In another example, the pressure is about 40 Torr. The soak process is usually conducted to the substrate surface for a time period in the range from about 1 second to about 90 seconds. In one example, the soak process will last for about 60 seconds or less. In another example, the soak process will last for about 30 seconds or less. In another aspect, the soak process will last for about 10 seconds. The soak process includes a soak compound, such as a reductant and usually has a carrier gas. The flow rate of the reductant is generally in the range from about 10 sccm to about 2,000 sccm, preferably in the range from about 50 sccm to about 500 sccm. The flow rate of the carrier gas is generally in the range from about 10 sccm to about 2,000 sccm, preferably in the range from about 50 sccm to about 500 sccm.

The barrier layer disposed on the substrate is reduced and/or adsorbs the reductant to form a conditioned layer for the subsequent nucleation layer. The conditioned barrier layer provides for a quicker and smoother deposition of the nucleation layer. In one example, diborane is introduced with hydrogen, each having a flow rate in a range from about 50 sccm to about 500 sccm. Preferably, the diborane and hydrogen gases are introduced in a 1:1 volumetric ratio. In another example, silane is introduced with hydrogen, each having a flow rate in a range from about 50 sccm to about 500 sccm. Preferably in step 120, the reductant or soak compound utilized in the soak process is diborane or silane.

In step 130, the tungsten-containing precursor is preferably tungsten hexafluoride and introduced at a rate in the range from about 5 sccm to about 200 sccm. The tungsten-containing precursor can be introduced with a carrier gas, such as argon with a flow rate in the range from about 50 sccm to about 1,000 sccm. In step 150, the reductant is preferably diborane or silane and introduced at a rate in the range from about 5 sccm to about 2,000 sccm, preferably in the range from about 50 sccm to about 500 sccm. The reductant can be introduced with a carrier gas, such as hydrogen, with a flow rate in the range from about 50 sccm to about 2,000 sccm. The pulses of a purge gas, preferably argon or nitrogen, at steps 140 and 160, are typically introduced at a rate from about 50 sccm to about 2,000 sccm, preferably at about 500 sccm. Steps 140 and 160 may include a continuous flow of purge gas whereas the tungsten-containing compound and the reducing gas are pulsed into a steady stream of carrier gas. Each processing step (steps 130 through 160) lasts from about 0.01 seconds to about 10 seconds, preferably in the range from about 0.1 seconds to about 1 second. Longer processing steps, such as about 30 seconds or about 60 seconds, achieve tungsten deposition. However, the throughput is reduced. The specific pressures and times are obtained through experimentation. In one example, a 300 mm diameter wafer needs about twice the flow rate as a 200 mm diameter wafer in order to maintain similar throughput.

An ALD process chamber used during embodiments described herein is available from Applied Materials, Inc. located in Santa Clara, Calif. A more detailed description of an ALD process chamber may be found in commonly assigned U.S. patent application Ser. No. 10/032,284, entitled “Gas Delivery Apparatus and Method for Atomic Layer Deposition”, filed on Dec. 21, 2001, U.S. patent application Ser. No. 10/281,079, entitled “Gas Delivery Apparatus for Atomic Layer Deposition”, filed on Oct. 25, 2002, and U.S. patent application Ser. No. 10/016,300, entitled “Lid Assembly For A Processing System To Facilitate Sequential Deposition Techniques”, filed on Dec. 12, 2001, which are hereby incorporated by reference in their entirety. Software routines are executed to initiate process recipes or sequences. The software routines, when executed, transform the general purpose computer into a specific process computer that controls the chamber operation so that a chamber process is performed. For example, software routines may be used to precisely control the activation of the electronic control valves for the execution of process sequences according to aspects of the invention. Alternatively, the software routines may be performed in hardware, as an application specific integrated circuit or other type of hardware implementation, or a combination of software or hardware.

FIG. 2 illustrates process 200 for the forming of a tungsten-containing material according to one embodiment described herein. During step 210, the substrate is loaded into a process chamber. The substrate usually contains a barrier layer disposed thereon and is exposed to a first soak process during step 220. The soak process includes delivering a reducing gas containing a reductant into the process chamber. The substrate surface forms a treated layer, such as a reduced barrier layer. During step 230, a nucleation layer (e.g., tungsten) is deposited on the substrate. Generally, the nucleation layer is deposited by a vapor deposition process that includes ALD, CVD or pulsed-CVD. In step 240, the nucleation layer is exposed to a second soak process with the same or a different reductant as used in step 220. Thereafter, a bulk layer (e.g., tungsten) is deposited on the nucleation layer during step 250. The bulk layer may be deposited by a CVD process or a PVD process.

During step 210, the substrate is positioned into the process chamber. The substrate surface may contain a barrier layer disposed thereon. Barrier layers usually contain a metal or metal nitride material that includes titanium, titanium nitride, titanium silicon nitride, tantalum, tantalum nitride, tantalum silicon nitride, and combinations thereof. A barrier layer may be formed by process techniques such as chemical vapor deposition (CVD), atomic layer deposition (ALD), physical vapor deposition (PVD), derivatives thereof and combinations thereof. The barrier layer is usually deposited to a thickness of at least about 30 Å, such as in a range from about 30 Å to about 100 Å. In one example, a barrier layer is deposited on the substrate surface by a CVD process by using tetrakis(dimethylamino)titanium (TDMAT) and ammonia. In another example, a barrier layer is deposited on the substrate surface by an ALD process by sequentially pulsing titanium tetrachloride (TiCl₄) and ammonia. In another example, a barrier layer is deposited on the substrate surface by a PVD process by sputtering from a titanium source in a nitrogen environment. The barrier layer may be plasma densified prior to performing a subsequent fabrication process.

The process conditions, such as temperature and pressure, set during step 210 may be used during step 220. The process chamber is adjusted to heat the substrate at a temperature in the range from about 100° C. to about 600° C., preferably in the range from about 200° C. to about 500° C., and more preferably in the range from about 300° C. to about 450° C. The process chamber is maintained at a pressure in the range from about 1 Torr to about 150 Torr, preferably in the range from about 5 Torr to about 90 Torr. In one example, the process chamber used during the soak process may be the same process chamber as used to deposit the barrier layer. In another example, the process chamber used during the soak process is used to deposit the subsequent nucleation layer during step 230.

During step 220, the substrate surface is exposed to a soak process containing a reductant and an optional carrier gas. The reductant adsorbs and/or reacts to the substrate surface, namely the barrier layer, to form a treated surface. The treated surface provides a quicker deposition process for an overall smooth and more uniform tungsten layer. The reductants may include silane compounds, borane compounds, phosphine compounds, ammonia and ammine compounds and hydrogen. Silane compounds include silane, disilane, trisilane, tetrasilane, chlorosilane, dichlorosilane, tetrachlorosilane, hexachlorodisilane and derivatives thereof, while borane compounds include borane, diborane, triborane, tetraborane, pentaborane, alkylboranes, such as triethylborane and derivatives thereof. The preferred reductants include silane, disilane, diborane and hydrogen. A carrier gas may be co-flowed with the reductant. Carrier gases include hydrogen, nitrogen, argon, helium and combinations thereof. For example, diborane is often used with a concentration of 5 vol % in argon or nitrogen.

The soak process in step 220 usually last for a period of time in the range from about 1 second to about 90 seconds. The barrier layer disposed on the substrate is reduced and/or adsorbs the reductant to form a conditioned layer for the subsequent nucleation layer. In one example performed prior to an ALD nucleation process, about 300 sccm of a 5 vol % diborane in argon is exposed to the substrate for about 30 seconds at about 15 Torr and about 350° C. In one example performed prior to a pulsed-CVD nucleation process, about 200 sccm of a 5 vol % diborane in nitrogen is exposed to the substrate for about 24 seconds at about 90 Torr and about 400° C.

During step 230, a nucleation layer is deposited on the substrate surface, namely on the treated barrier layer. The nucleation layer may be deposited by a vapor deposition process that includes ALD, CVD and/or pulsed-CVD. The process chamber used to deposit the nucleation layer may be the same process chamber used in the soak processes as described in steps 220 and 240. The nucleation layer may comprise tungsten, tungsten alloys, tungsten-containing materials (e.g., tungsten boride or tungsten silicide) and combinations thereof. The nucleation layer is typically deposited to a thickness in a range from about 10 Å to about 200 Å. In one example, an ALD process utilizing WF₆ and B₂H₆ deposits a nucleation layer with a thickness in a range from about 10 Å to about 20 Å, such as about 12 Å. In another example, an ALD process utilizing WF₆ and SiH₄ deposits a nucleation layer with a thickness in a range from about 10 Å to about 50 Å, such as about 30 Å. In another example, a pulsed-CVD (e.g., co-flowed) process utilizing WF₆ and SiH₄ or WF₆ and B₂H₆ deposits a nucleation layer with a thickness in a range from about 30 Å to about 200 Å, such as about 50 Å. Preferably, the ALD process as described herein during process 100 may be used to deposit the nucleation layer.

During step 240, the substrate surface is exposed to a post soak process or a second soak process containing a reductant and an optional carrier gas. The reductant adsorbs and/or reacts to the substrate surface, namely the nucleation layer, to form a treated surface. The reductants, as described above, may also include silane compounds, borane compounds, phosphine compounds, ammonia and ammine compounds and hydrogen. The preferred reductants include silane, disilane, diborane and hydrogen. A carrier gas may be co-flowed with the reductant and include hydrogen, nitrogen, argon, helium and combinations thereof. For example, diborane is often used with a concentration of 5 vol % in argon or nitrogen.

The soak process in step 240 usually last for a period of time in the range from about 1 second to about 90 seconds. The process chamber is adjusted to heat the substrate at a temperature in the range from about 100° C. to about 600° C., preferably in the range from about 200° C. to about 500° C., more preferably in the range from about 300° C. to about 450° C. The process chamber is maintained at a pressure in the range from about 1 Torr to about 150 Torr, preferably in the range from about 5 Torr to about 90 Torr. The barrier layer disposed on the substrate is reduced and/or adsorbs the reductant to form a conditioned layer for the subsequent bulk layer. In one example performed after an ALD nucleation process, about 300 sccm of a 5 vol % diborane in nitrogen is exposed to the substrate for about 30 seconds at about 30 Torr and about 300° C. In one example performed after a pulsed-CVD nucleation process, about 200 sccm of a 5 vol % diborane in argon is exposed to the substrate for about 30 seconds at about 15 Torr and about 400° C. In another example performed after a pulsed-CVD nucleation process, about 300 sccm of a 5 vol % diborane in argon is exposed to the substrate for about 10 seconds at about 90 Torr and about 400° C.

During step 250, a bulk layer is deposited on the substrate surface, namely on the treated nucleation layer. The bulk layer may be deposited by a vapor deposition process that includes CVD, pulsed-CVD and/or PVD. The process chamber used to deposit the bulk layer may be the same process chamber used in the post soak process as described in step 240. The bulk layer comprises tungsten, tungsten alloys, tungsten-containing materials (e.g., tungsten boride, tungsten silicide or tungsten phosphide) and combinations thereof. The bulk layer is typically deposited to a thickness in the range from about 100 Å to about 10,000 Å, preferably from about 1,000 Å to about 5,000 Å. In one example, a CVD process utilizing WF₆ and B₂H₆ is used to deposit a bulk layer on the treated nucleation layer. In another example, a CVD process utilizing WF₆ and SiH₄ is used to deposit a bulk layer on the treated nucleation layer. In another example, a PVD process utilizing a tungsten source is used to deposit a bulk layer on the treated nucleation layer. Processes for soaking a tungsten nucleation layer and depositing a tungsten bulk layer thereon is further described in the commonly assigned U.S. Pat. No. 6,156,382, which is incorporated by reference herein.

In an alternative embodiment, a tungsten-containing film is deposited by depositing more than one nucleation layer and may include multiple cycles of a vapor deposition process. In one example, the barrier layer may be exposed to a soak process prior to forming a first nucleation layer by a pulsed-CVD process. The process chamber is heated to a temperature in a range from about 400° C. to about 450° C., for example, about 425° C. and maintained at a pressure in a range from about 10 Torr to about 20 Torr, such as about 15 Torr. The pulsed-CVD process may include exposing the substrate to a co-flow of a tungsten-containing compound and a reductant for a period of time from about 1 second to about 3 seconds, for example about 1.5 seconds. The flow of the reagents include the tungsten-containing compound with a flow rate from about 30 sccm to about 90 sccm, such as about 60 sccm, while the reductant is at a flow rate from about 10 sccm to about 50 sccm, such as about 30 sccm. The co-flow is stopped and the process chamber purged. Then the reductant is pulsed into the chamber for a period of time from about 1 second to about 3 seconds, for example about 1 second. The reductant may have a flow rate from about 10 sccm to about 50 sccm, such as about 30 sccm. The flow of the reductant is stopped and the chamber purged for about 0.5 seconds. The cycle is repeated until a predetermined thickness of the first nucleation layer is formed. For example, the process is repeated 3 times to form a layer with a thickness about 30 Å. The preferred tungsten-containing compound is tungsten hexafluoride and the preferred reductant is silane and/or diborane. The reductant is optionally used during a soak process prior or subsequent the deposition of the first nucleation layer.

A second nucleation layer may be formed on the first nucleation layer. The process chamber may be kept at the same temperature, but the pressure of the process chamber is usually increased. The process chamber is maintained at a temperature in a range from about 400° C. to about 450° C., for example, about 425° C. and the a pressure is in a range from about 20 Torr to about 50 Torr, such as about 30 Torr. The CVD process may include exposing the substrate to a co-flow of a tungsten-containing compound and a reductant for a period of time from about 4 seconds to about 8 seconds, for example about 6 seconds. The flow of the reagents include the tungsten-containing compound with a flow rate from about 30 sccm to about 70 sccm, such as about 50 sccm, while the reductant has a flow rate from about 10 sccm to about 50 sccm, such as about 25 sccm. A second nucleation layer is deposited on the first nucleation layer and has a thickness in a range from about 50 Å to about 1,000 Å, preferably from about 150 Å to about 300 Å. The preferred tungsten-containing compound is tungsten hexafluoride and the preferred reductant is silane and/or diborane. The reductant is optionally used during a soak process prior or subsequent the deposition of the second nucleation layer.

Finally, a bulk layer may be deposited on the second nucleation layer. The bulk layer may be deposited by a tradition CVD process. In one example, the process chamber is maintained at a temperature in a range from about 400° C. to about 450° C., for example, about 425° C. and the pressure is maintained in a range from about 100 Torr to about 350 Torr, such as about 200 Torr. The flow of the reagents include the tungsten-containing compound with a flow rate from about 200 sccm to about 800 sccm, such as about 400 sccm, while the reductant has a flow rate from about 2,000 sccm to about 8,000 sccm, such as about 4,000 sccm. The preferred tungsten-containing compound is tungsten hexafluoride and the preferred reductant is hydrogen.

Process Integration

A tungsten nucleation layer as described above has shown particular utility when integrated with traditional bulk fill techniques to form features with excellent film properties. An integration scheme can include ALD or pulsed-CVD processes to deposit a nucleation layer while a bulk layer may be deposited by CVD or PVD processes. Integrated processing systems capable of performing such an integration scheme include an Endura®, Endura SL®, Centura® and Producer® processing systems, each available from Applied Materials, Inc. located in Santa Clara, Calif. Any of these systems can be configured to include at least one ALD or pulsed-CVD chamber for depositing the nucleation layer and at least one CVD chamber or PVD chamber for bulk fill.

FIG. 3A is a schematic top-view diagram of an exemplary multi-chamber processing system 300. A similar multi-chamber processing system is disclosed in commonly assigned U.S. Pat. No. 5,186,718, which is incorporated by reference herein. The system 300 generally includes load lock chambers 302, 304 for the transfer of substrates into and out from the system 300. Typically, since the system 300 is under vacuum, the load lock chambers 302, 304 may “pump down” the substrates introduced into the system 300. A first robot 310 may transfer the substrates between the load lock chambers 302, 304, and a first set of one or more substrate processing chambers 312, 314, 316, 318 (four are shown). Each processing chamber 312, 314, 316, 318, can be outfitted to perform a number of substrate processing operations such as cyclical layer deposition, CVD, PVD, etch, pre-clean, de-gas, orientation and other substrate processes. The first robot 310 also transfers substrates to/from one or more transfer chambers 322, 324.

The transfer chambers 322, 324, are used to maintain ultrahigh vacuum conditions while allowing substrates to be transferred within the system 300. A second robot 330 may transfer the substrates between the transfer chambers 322, 324 and a second set of one or more processing chambers 332, 334, 336, 338. Similar to processing chambers 312, 314, 316, 318, the processing chambers 332, 334, 336, 338 can be outfitted to perform a variety of substrate processing operations, such as cyclical deposition, CVD, PVD, etch, pre-clean, de-gas, and orientation, for example. Any of the substrate processing chambers 312, 314, 316, 318, 332, 334, 336, 338 may be removed from the system 300 if not necessary for a particular process to be performed by the system 300.

In one arrangement, each processing chamber 332 and 338 may be a cyclical deposition chamber adapted to deposit a nucleation layer; each processing chamber 334 and 336 may be a cyclical deposition chamber, a chemical vapor deposition chamber or a physical vapor deposition chamber adapted to form a bulk layer; each processing chamber 312 and 314 may be a physical vapor deposition chamber, a chemical vapor deposition chamber, or a cyclical deposition chamber adapted to deposit a dielectric layer; and each processing chamber 316 and 318 may be an etch chamber outfitted to etch apertures or openings for interconnect features. This one particular arrangement of the system 300 is provided to illustrate the invention and should not be used to limit the scope of the invention.

Another integrated system may include nucleation deposition as well as bulk fill deposition in a single chamber. A chamber configured to operate in both a cyclical deposition mode as well as a conventional CVD mode can be used. One example of such a chamber is described in commonly assigned U.S. patent application Ser. No. 10/016,300, filed on Dec. 12, 2001, which is incorporated herein by reference.

In another integration scheme, one or more cyclical deposition nucleation chambers are integrated onto a first processing system while one or more bulk layer deposition chambers are integrated onto a second processing system. In this configuration, substrates are first processed in the first system where a nucleation layer is deposited on a substrate. Thereafter, the substrates are moved to the second processing system where bulk deposition occurs.

FIG. 3B is a schematic top-view diagram of an exemplary multi-chamber processing system 350. The system 350 generally includes load lock chambers 352, 354 for the transfer of substrates into and out from the system 350. Typically, since the system 350 is under vacuum, the load lock chambers 352, 354 may “pump down” the substrates introduced into the system 350. A robot 360 may transfer the substrates between the load lock chambers 352, 354, and substrate processing chambers 362, 364, 366, 368, 370 and 372. Each processing chamber 362, 364, 366, 368, 370 and 372 can be outfitted to perform a number of substrate processing operations such as cyclical layer deposition, CVD, PVD, etch, pre-clean, de-gas, heat, orientation and other substrate processes. The robot 360 also transfers substrates to/from a transfer chamber 356. Any of the substrate processing chambers 362, 364, 366, 368, 370 and 372 may be removed from the system 350 if not necessary for a particular process to be performed by the system 350.

In one arrangement, each processing chamber 364 and 370 may be a cyclical deposition chamber adapted to deposit a nucleation layer; each processing chamber 366 and 368 may be a cyclical deposition chamber, a chemical vapor deposition chamber or a physical vapor deposition chamber adapted to form a bulk fill deposition layer. This one particular arrangement of the system 350 is provided to illustrate the invention and should not be used to limit the scope of the invention.

Alternatively, a carousel type batch processing system having a plurality of stations in a single chamber can be adapted to incorporate nucleation and bulk layer deposition into a single processing system. In such a processing system a purge gas curtain, such as an argon gas curtain, can be established between each station creating a micro or mini environment at each station. The substrates are loaded into the system sequentially and then rotated through each station and processed at least partially at each station. For example, a substrate may be exposed to a cyclical deposition nucleation step at a first station and then to partial bulk fill CVD steps at each of the subsequent stations. Alternatively, nucleation may occur at more than one station and bulk fill may occur at one or more stations. Still further, the nucleation layer and the bulk layer may be deposited in separate carousel type systems. In another aspect, the soak and the nucleation steps are completed in one carousel while the bulk steps are done on another carousel, wherein both carousels are part of the same process system. Each platen can be temperature controlled to provide at least some process control at each station. However, the process pressure typically remains the same between stations because the stations are housed in a single chamber. Some pressure control may be available in a micro or mini environment present at each station due to the inert gas curtain.

Regardless of the integration scheme, the nucleation layer is typically deposited to a thickness in a range from about 10 Å to about 200 Å and the bulk layer has a thickness in a range from about 100 Å to about 10,000 Å, preferably in the range from about 1,000 Å to about 5,000 Å. However, the thickness of these films can vary depending on the feature sizes and aspect ratios of a given application. Accordingly, the films are suitably sized to accommodate the geometries of a given application. The following are some exemplary geometries and applications that can benefit from a nucleation layer deposited according to embodiments described herein. The following descriptions are intended for illustrative purposes only, and are not intended to limit the uses of the present invention.

FIGS. 4A-C show cross sectional views of a semiconductor feature that one embodiment of the process is utilized to fill a via 460. In FIG. 4A, the substrate 450 includes at least one via 460. A barrier layer 451, such as titanium nitride, is deposited by ALD, CVD or PVD techniques to the substrate 450 with via 460. Prior to the nucleation of a tungsten layer 452, as depicted in FIG. 4B, a soak process is administered to barrier layer 451. The soak process renders the sidewalls, of the barrier layer 451 within the via 460, to adhere and grow the tungsten layer 452 at about the same rate as the barrier layer 451 outside the via 460. When the soak process is omitted, growth of tungsten layer 452 on the sidewalls is not constant with respect to the growth of tungsten layer 452 outside the via 460. Once the nucleation of tungsten layer 452 has been deposited, then a secondary soak or post soak process is conducted to treat tungsten layer 452. The post soak process provides tungsten layer 452 to more smoothly continue growth while filling the via 460, as demonstrated in FIG. 4C. In one example, an ALD process is continued after deposition of a tungsten nucleation layer to deposit the tungsten bulk layer. In another example, an ALD process is used to deposit the tungsten nucleation layer and a CVD process is used to deposit the tungsten bulk layer. In another example, an ALD process is used to deposit the tungsten nucleation layer and a PVD process is used to deposit the tungsten bulk layer. In another example, a pulsed-CVD process is used to deposit the tungsten nucleation layer and a conventional CVD process is used to deposit the tungsten bulk layer. In another example, a pulsed-CVD process is used to deposit the tungsten nucleation layer and a PVD process is used to deposit the tungsten bulk layer.

Tungsten Metal Gate

FIG. 5 shows a cross sectional view of an exemplary metal oxide gate device 400 utilizing a nucleation layer deposited according to embodiments described herein. The device 400 generally includes an exposed gate 410 surrounded by spacers 416 and silicon source/drain areas 420 formed within a substrate surface 412. The spacers 416 typically include an oxide, such as silicon dioxide, or a nitride, such as silicon nitride.

The metal gate 410 includes an oxide layer 411, a polysilicon layer 414, a titanium nitride barrier layer 415 and a tungsten layer 422. The oxide layer 411 separates the substrate 412 from the polysilicon layer 414. The oxide layer 411 and the polysilicon layer 414 are deposited using conventional deposition techniques.

The titanium nitride barrier layer 415 is deposited on the polysilicon layer 414. The titanium nitride barrier layer 415 may be a bi-layer stack formed by depositing a PVD titanium layer followed by a CVD titanium nitride layer. The titanium nitride barrier layer 415 may also be deposited using a cyclical deposition technique, such as the process shown and described in commonly assigned and co-pending U.S. patent application Ser. No. 10/032,293, filed on Dec. 21, 2001, entitled “Chamber Hardware Design for Titanium Nitride Atomic Layer Deposition,” published as U.S. Patent Publication 20030116087, which is incorporated by reference herein.

A soak process is administered to the substrate surface. The soak includes a silane compound or a borane compound along with at least one carrier gas. A preferred silane compound is silane, a preferred borane compound is diborane and a preferred carrier gas is either hydrogen, nitrogen and/or argon. In one aspect, silane has a flow rate in the range from about 25 sccm to about 500 sccm and hydrogen has a flow rate in the range from about 200 sccm to about 700 sccm. The soak process is conducted at a temperature in the range from about 100° C. to about 500° C., preferably at about 300° C., a pressure in the range from about 1 Torr to about 150 Torr, preferably from about 30 Torr to about 120 Torr and for a time period from about 1 second to about 90 seconds. In another aspect, diborane has a flow rate in the range from about 25 sccm to about 500 sccm and hydrogen and/or argon has a flow rate in the range from about 200 sccm to about 700 sccm. The soak process is conducted at a temperature in the range from about 100° C. to about 500° C., preferably at about 300° C., a pressure in the range from about 1 Torr to about 120 Torr, preferably at about 5 Torr to about 50 Torr, and a period of time from about 1 second to about 90 seconds, preferably less than about 60 seconds.

In one example, a nucleation layer 417 is then cyclically deposited over the barrier layer 415 following treatment of the substrate surface with a soak process. In one aspect, the nucleation layer 417 is cyclically deposited using alternating pulses of tungsten hexafluoride and diborane. The tungsten hexafluoride is pulsed at a rate of between about 1 sccm and about 100 sccm, such as between about 5 sccm and about 50 sccm, for about 0.3 seconds. A carrier gas, such as argon, is provided along with the tungsten hexafluoride at a rate of about 100 sccm to about 1,000 sccm, such as between about 100 sccm to about 500 sccm. The diborane is pulsed at a rate of about 50 sccm and about 1,000 sccm, such as between about 400 sccm and about 600 sccm, for about 0.3 seconds. A carrier gas, such as hydrogen, is provided along with the diborane at a rate between about 50 sccm to about 500 sccm, such as between about 100 sccm to about 300 sccm. The substrate is maintained at a temperature between about 100° C. and about 400° C., preferably at about 300° C., at a chamber pressure between about 1 Torr and about 120 Torr, preferably between about 5 Torr and about 50 Torr. In between pulses of the tungsten hexafluoride and the diborane, argon is pulsed for about 0.5 seconds to purge or otherwise remove any reactive compounds from the processing chamber.

In another aspect, the nucleation layer 417 is cyclically deposited using alternating pulses of tungsten hexafluoride and silane. The tungsten hexafluoride is pulsed as described above with argon for about 0.5 seconds. The silane is pulsed at a rate of about 1 sccm to about 100 sccm, such as between about 5 sccm to about 50 sccm, for about 0.5 seconds. A carrier gas, such as hydrogen, is provided along with the silane at a rate of about 100 sccm and about 1,000 sccm, such as between about 100 sccm and about 500 sccm. Argon is pulsed at a rate of about 100 sccm to about 1,000 sccm, such as between about 300 sccm to about 700 sccm, for about 0.5 seconds between the pulses of the tungsten hexafluoride and the pulses of silane. The substrate is maintained at a temperature between about 100° C. and about 400° C., preferably at about 300° C., at a chamber pressure between about 1 Torr and about 30 Torr.

In another example, a nucleation layer 417 is deposited by a pulsed-CVD process on the barrier layer 415 following treatment of the substrate surface with a soak process. The pulsed-CVD process includes co-flowing WF₆ and B₂H₆ or WF₆ and SiH₄ at a temperature in a range from about 300° C. to about 500° C., preferably from about 400° C. to about 450° C. The pulsed-CVD process pulses the co-flowing precursors at a time period from about 0.5 seconds to about 3 seconds, preferably about 1.5.

A second soak process or post soak process is administered to the substrate surface. The soak process includes a reductant, such as silane compound or a borane compound along with at least one carrier gas. Preferably, the reductant is diborane and a preferred carrier gas is hydrogen, nitrogen and/or argon. In one example, a reducing gas containing 5 vol % of diborane in argon has a flow rate in the range from about 100 sccm to about 500 sccm, preferably about 300 sccm. The soak process is conducted at a temperature in the range from about 100° C. to about 500° C., preferably about 300° C., a pressure in the range from about 1 Torr to about 120 Torr, preferably at about 10 Torr to about 50 Torr, and for a time period from about 1 second to about 90 seconds, preferably less than about 30 seconds.

A nucleation layer formed utilizing soak processes has advantages over a nucleation layer formed without the soak processes. The tungsten film shows less stress for the integrated film, as well as, less fluorine content at the interface of the nucleation layer. Also, the nucleation layer deposited post a soak treatment has higher uniformity coverage and is deposited quicker due to a reduced incubation period.

A tungsten bulk fill 422 is then deposited on the treated tungsten nucleation layer 417. Although any metal deposition process, such as conventional chemical vapor deposition or physical vapor deposition, may be used, the tungsten bulk fill 422 may be deposited by alternately adsorbing a tungsten-containing compound and a reducing compound as described above. A more detailed description of tungsten deposition using a cyclical deposition technique may be found in commonly assigned U.S. patent application Ser. No. 10/016,300, entitled “Lid Assembly For A Processing System To Facilitate Sequential Deposition Techniques,” filed on Dec. 12, 2001 and in commonly assigned U.S. patent application Ser. No. 10/082,048, entitled “Deposition Of Tungsten Films For Dynamic Random Access Memory (DRAM) Application,” filed on Feb. 20, 2002, which are both incorporated herein by reference. Fewer volcanos appear on the surface of the tungsten film deposited utilizing a soak process, as compared to tungsten films deposited without exploiting a soak process, post tungsten bulk-fill.

Following deposition, the top portion of the resulting structure 400 may be planarized. A chemical mechanical polishing (CMP) apparatus may be used, such as the Mirra™ System available from Applied Materials, Santa Clara, Calif., for example. Portions of the tungsten bulk fill 422 are removed from the top of the structure leaving a fully planar surface. Optionally, the intermediate surfaces of the structure may be planarized between the depositions of the subsequent layers described above.

FIG. 6 is a cross sectional view of a conventional DRAM device having a transistor 520 positioned adjacent a top portion of a trench capacitor 530. The access transistor 520 for the DRAM device 510 is positioned adjacent a top portion of the trench capacitor 530. Preferably, the access transistor 520 comprises an n-p-n transistor having a source region 522, a gate region 524 and a drain region 526. The gate region 524 is a P− doped silicon epi-layer disposed over the P+ substrate. The source region 522 of the access transistor 520 is an N+ doped material disposed on a first side of the gate region 524 and the drain region 526 is an N+ doped material disposed on a second side of the gate region 524, opposite the source region 522.

The source and drain regions 522, 524 may be connected to a tungsten plug 560. Each tungsten plug 560 includes a titanium liner 562, a tungsten nucleation layer 564, and a bulk tungsten fill 566. The titanium liner 562 may be a bi-layer stack comprising PVD titanium followed by CVD titanium nitride. Alternatively, the titanium liner 562 may be a bi-layer stack comprising ALD deposited titanium followed by ALD deposited titanium nitride. The tungsten nucleation layer 564 is formed by using a soak process and an ALD process or a soak process and a pulsed-CVD process as described above. The tungsten bulk fill 566 may be deposited using a post soak process and any conventional deposition techniques, including ALD, CVD and PVD.

The trench capacitor 530 generally includes a first electrode 532, a second electrode 534 and a dielectric material 536 disposed therebetween. The P+ substrate serves as a first electrode 532 of the trench capacitor 530 and is connected to a ground connection 541. A trench 538 is formed in the P+ substrate and filled with a heavily doped N+ polysilicon that serves as the second electrode 534 of the trench capacitor 530. The dielectric material 536 is disposed between the first electrode 532 (i.e., P+ substrate) and the second electrode 534 (i.e., N+ polysilicon).

The trench capacitor 530 also includes a first tungsten nitride barrier layer 540 disposed between the dielectric material 536 and the first electrode 532. Preferably, a second tungsten nitride barrier layer 542 is disposed between the dielectric material 536 and the second electrode 534. Alternatively, the barrier layers 540, 542 are a combination film, such as W/WN.

Although the above-described DRAM device utilizes an n-p-n transistor, a P+ substrate as a first electrode, and an N+ polysilicon as a second electrode of the capacitor, other transistor designs and electrode materials are contemplated by the present invention to form DRAM devices. Additionally, other devices, such as crown capacitors for example, are contemplated by the present invention.

EXAMPLES

The following examples were conducted to substrates that contained a barrier layer deposited on the surface. The barrier layer was formed by first depositing a titanium layer by a PVD process on a 300 mm substrate surface to a thickness of about 20 Å. Subsequently, a titanium nitride layer was deposited on the titanium layer using a CVD process of co-flowing PDMAT and ammonia. The tantalum nitride layer was deposited to a thickness of about 80 Å.

W-ALD Examples Example 1

The substrate was placed into an ALD chamber and exposed to a soak process under the following conditions:

Reagent: B₂H₆;

Pressure: about 15 Torr;

Temperature: about 300° C.;

Flow rates: 300 sccm 5% B₂H₆ in Ar; and

Duration: about 30 seconds.

Next, a tungsten nucleation layer was formed on the barrier layer in the same ALD chamber from the previous soak process using an ALD process under the following conditions:

Reagents: WF₆ and B₂H₆;

Pressure: about 5 Torr;

Temperature: about 300° C.;

Flow rates:

-   -   pulse A: 20 sccm WF₆ and 300 sccm Ar;     -   pulse B: 150 sccm B₂H₆ and 150 sccm H₂;     -   Ar-purge: 500 sccm;

Cycle duration: Ar-purge: 0.5 seconds;

-   -   pulse A: 0.2 seconds;     -   Ar-purge: 0.5 seconds; and     -   pulse B: 0.2 seconds.

The cycle was repeated 4 times to form a nucleation layer with a thickness of about 12 Å. Thereafter, the substrate was maintained in the ALD chamber and exposed to a second soak process under the following conditions:

Reagent: B₂H₆;

Pressure: about 30 Torr;

Temperature: about 300° C.;

Flow rates: 300 sccm 5% B₂H₆ in Ar; and

Duration: about 30 seconds.

Finally, the substrate was transferred into a CVD chamber and a bulk tungsten layer was deposited to a thickness of about 2,500 Å on the nucleation layer using a CVD process at about 400° C. The resulting tungsten bulk fill film exhibited a uniformity variance of less than about 2 percent.

Example 2

The substrate was placed into an ALD chamber and exposed to a soak process under the following conditions:

Reagent: B₂H₆;

Pressure: about 15 Torr;

Temperature: about 300° C.;

Flow rates: 300 sccm 5% B₂H₆ in Ar; and

Duration: about 30 seconds.

Next, a tungsten nucleation layer was formed on the barrier layer in the same ALD chamber as used in the prior soak process using an ALD process under the following conditions:

Reagents: WF₆ and SiH₄;

Pressure: about 10 Torr;

Temperature: about 300° C.;

Flow rates:

-   -   pulse A: 30 sccm WF₆ and 300 sccm Ar;     -   pulse B: 20 sccm SiH₄ and 300 sccm H₂;     -   Ar purge: 500 sccm;

Cycle duration:

-   -   Ar-purge: 0.5 seconds;     -   pulse A: 0.3 seconds;     -   Ar-purge: 0.5 seconds; and     -   pulse B: 0.3 seconds.

The cycle was repeated 4 times to form a nucleation layer with a thickness of about 30 Å. Thereafter, the substrate was transferred to a CVD chamber and exposed to a second soak process under the following conditions:

Reagent: B₂H₆;

Pressure: about 30 Torr;

Temperature: about 300° C.;

Flow rates: 300 sccm 5% B₂H₆ in Ar; and

Duration: about 30 seconds.

Finally, the substrate was maintained in the CVD chamber and a bulk tungsten layer was deposited to a thickness of about 2,500 Å on the nucleation layer using a CVD process at about 400° C. The resulting tungsten bulk fill film exhibited a uniformity variance of less than about 4 percent.

CVD Examples Example 3

The substrate was placed into a CVD chamber and exposed to a soak process under the following conditions:

Reagent: B₂H₆;

Pressure: about 90 Torr;

Temperature: about 400° C.;

Flow rates: 200 sccm 5% B₂H₆ in Ar; and

Duration: about 24 seconds.

Next, a tungsten nucleation layer was formed on the barrier layer in the CVD chamber from the previous soak process using a pulsed-CVD process under the following conditions:

Reagents: WF₆ and SiH₄;

Pressure: about 30 Torr;

Temperature: about 400° C.;

Flow rates: 60 sccm WF₆ and 30 sccm SiH₄;

Pulse duration: 1.5 seconds;

The pulsed-CVD process was continued until the nucleation layer had a thickness of about 50 Å. Thereafter, the substrate was kept in the CVD chamber and a second nucleation layer was deposited on the first nucleation layer. The second nucleation layer was deposited by a traditional CVD process to a thickness of about 200 Å under the following conditions:

Reagents: WF₆ and SiH₄;

Pressure: about 30 Torr;

Temperature: about 400° C.;

Flow rates: 60 sccm WF₆ and 30 sccm SiH₄.

Subsequently, a bulk tungsten layer was deposited to a thickness of about 2,500 Å on the second nucleation layer using a CVD process at about 400° C.

Example 4

The substrate was placed into a CVD chamber and exposed to a soak process under the following conditions:

Reagent: B₂H₆;

Pressure: about 90 Torr;

Temperature: about 400° C.;

Flow rates: 200 sccm 5% B₂H₆ in Ar; and

Duration: about 24 seconds.

Next, a tungsten nucleation layer was formed on the barrier layer in the previously used CVD chamber using a pulsed-CVD process under the following conditions:

Reagents: WF₆ and B₂H₆;

Pressure: about 30 Torr;

Temperature: about 400° C.;

Flow rates: 60 sccm WF₆ and 30 sccm B₂H₆;

Pulse duration: 1.5 seconds;

The pulsed-CVD process was continued until the nucleation layer had a thickness of about 50 Å. Thereafter, the substrate was kept in the CVD chamber and a second nucleation layer was deposited on the first nucleation layer. The second nucleation layer was deposited by a traditional CVD process to a thickness of about 200 Å under the following conditions:

Reagents: WF₆ and B₂H₆;

Pressure: about 30 Torr;

Temperature: about 400° C.;

Flow rates: 60 sccm WF₆ and 30 sccm B₂H₆.

Example 5

The substrate was placed into a CVD chamber and exposed to a soak process under the following conditions:

Reagent: B₂H₆;

Pressure: about 90 Torr;

Temperature: about 400° C.;

Flow rates: 200 sccm 5% B₂H₆ in Ar; and

Duration: about 24 seconds.

Next, a tungsten nucleation layer was formed on the barrier layer in the same CVD chamber used during the soak process using a pulsed-CVD process under the following conditions:

Reagents: WF₆ and SiH₄;

Pressure: about 30 Torr;

Temperature: about 400° C.;

Flow rates: 60 sccm WF₆ and 30 sccm SiH₄;

Pulse duration: 1.5 seconds;

The pulsed-CVD process was continued until the nucleation layer had a thickness of about 150 Å. Thereafter, the substrate was kept in the CVD chamber and exposed to a second soak process under the following conditions:

Reagent: B₂H₆;

Pressure: about 90 Torr;

Temperature: about 400° C.;

Flow rates: 300 sccm 5% B₂H₆ in Ar; and

Duration: about 30 seconds.

Finally, the substrate was maintained in the CVD chamber and a bulk tungsten layer was deposited to a thickness of about 2,500 Å on the nucleation layer using a CVD process at about 400° C. The resulting tungsten bulk fill film exhibited a uniformity variance of less than about 4 percent.

Example 6

The substrate was placed into a CVD chamber and exposed to a soak process under the following conditions:

Reagent: B₂H₆;

Pressure: about 90 Torr;

Temperature: about 400° C.;

Flow rates: 200 sccm 5% B₂H₆ in Ar; and

Duration: about 24 seconds.

Next, a tungsten nucleation layer was formed on the barrier layer in the CVD chamber used during the prior soak process using a pulsed-CVD process under the following conditions:

Reagents: WF₆ and B₂H₆;

Pressure: about 30 Torr;

Temperature: about 400° C.;

Flow rates: 60 sccm WF₆ and 30 sccm B₂H₆;

Pulse duration: 1.5 seconds;

The pulsed-CVD process was continued until the nucleation layer had a thickness of about 150 Å. Thereafter, the substrate was kept in the CVD chamber and exposed to a second soak process under the following conditions:

Reagent: B₂H₆;

Pressure: about 15 Torr;

Temperature: about 400° C.;

Flow rates: 200 sccm 5% B₂H₆ in Ar; and

Duration: about 10 seconds.

Finally, the substrate was maintained in the CVD chamber and a bulk tungsten layer was deposited to a thickness of about 2,500 Å on the nucleation layer using a CVD process at about 400° C. The resulting tungsten bulk fill film exhibited a uniformity variance of less than about 2 percent.

Example 7

The substrate was placed into a CVD chamber and exposed to a soak process under the following conditions:

Reagent: B₂H₆;

Pressure: about 15 Torr;

Temperature: about 400° C.;

Flow rates: 200 scorn 5% B₂H₆ in Ar; and

Duration: about 1 second.

Next, the soak process is stopped for 0.5 seconds, the chamber purged and then a tungsten nucleation layer was formed on the barrier layer in the CVD chamber used during the prior soak process using a pulsed-CVD process under the following conditions:

Reagents: WF₆ and B₂H₆;

Pressure: about 15 Torr;

Temperature: about 400° C.;

Flow rates: 60 sccm WF₆ and 30 sccm B₂H₆;

Pulse duration: 1.5 seconds;

The first nucleation process was stopped and the chamber purged for about 0.5 seconds. Then the soak process and the pulsed-CVD process were repeated in a cycle for three times to form a first nucleation layer with a thickness of about 50 Å. Thereafter, the substrate was kept in the CVD chamber and exposed to a traditional CVD process to form a second nucleation layer with a thickness of about 200 Å on the first nucleation layer under the following conditions:

Reagents: WF₆ and B₂H₆;

Pressure: about 30 Torr;

Temperature: about 400° C.;

Flow rates: 60 sccm WF₆ and 30 sccm B₂H₆;

Duration: 6 seconds;

Finally, the substrate was maintained in the CVD chamber and a bulk tungsten layer was deposited to a thickness of about 2,500 Å on the second nucleation layer using a CVD process under the following conditions:

Reagents: WF₆ and H₂;

Pressure: about 300 Torr;

Temperature: about 400° C.;

Flow rates: 400 sccm WF₆ and 4,000 sccm H₂;

Pulse duration: 30 seconds.

Example 8

The substrate was placed into a CVD chamber and exposed to a soak process under the following conditions:

Reagent: SiH₄;

Pressure: about 15 Torr;

Temperature: about 425° C.;

Flow rates: 30 sccm SiH₄; and

Duration: about 1 second.

Next, the soak process is stopped for 0.5 seconds, the chamber purged and then a tungsten nucleation layer was formed on the barrier layer in the CVD chamber used during the prior soak process using a pulsed-CVD process under the following conditions:

Reagents: WF₆ and SiH₄;

Pressure: about 15 Torr;

Temperature: about 425° C.;

Flow rates: 60 sccm WF₆ and 30 sccm SiH₄;

Pulse duration: 1.5 seconds;

The first nucleation process was stopped and the chamber purged for about 0.5 seconds. Then the soak process and the pulsed-CVD process were repeated in a cycle for three times to form a first nucleation layer with a thickness of about 50 Å. Thereafter, the substrate was kept in the CVD chamber and exposed to a traditional CVD process to form a second nucleation layer with a thickness of about 200 Å on the first nucleation layer under the following conditions:

Reagents: WF₆ and SiH₄;

Pressure: about 30 Torr;

Temperature: about 425° C.;

Flow rates: 60 sccm WF₆ and 30 sccm SiH₄;

Duration: 8 seconds;

Finally, the substrate was maintained in the CVD chamber and a bulk tungsten layer was deposited to a thickness of about 2,500 Å on the second nucleation layer using a CVD process under the following conditions:

Reagents: WF₆ and H₂;

Pressure: about 300 Torr;

Temperature: about 400° C.;

Flow rates: 400 sccm WF₆ and 4,000 sccm H₂;

Pulse duration: 30 seconds.

While the foregoing is directed to embodiments of the invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow. 

1. A method for forming a tungsten-containing material on a substrate, comprising: positioning a substrate containing a substrate surface with a feature definition formed therein within a process chamber; depositing a tungsten nitride layer over the substrate surface and in the feature definition by sequentially exposing the substrate to tungsten hexafluoride and ammonia during an atomic layer deposition process; depositing a first nucleation layer over the tungsten nitride layer during a pulsed-CVD processes or an atomic layer deposition process utilizing tungsten hexafluoride and diborane or tungsten hexafluoride and silane; exposing the substrate to a reducing gas to form a reducing agent layer on the first nucleation layer during a soak process; and depositing a tungsten bulk layer over the reducing agent layer.
 2. The method of claim 1, wherein the tungsten nitride layer has a thickness of about 200 Å or less.
 3. The method of claim 1, wherein the tungsten bulk layer is deposited by a chemical vapor deposition process.
 4. The method of claim 1, wherein the reducing gas is selected from the group consisting of hydrogen, silane, disilane, dichlorosilane, ammonia, borane, diborane, derivatives thereof, and combinations thereof.
 5. The method of claim 1, further comprising exposing the substrate to a reducing agent prior to the depositing a tungsten nitride layer over the substrate surface and in the feature definition.
 6. The method of claim 5, wherein the reducing agent comprises one or more gases selected from the group consisting of hydrogen, silane, disilane, dichlorosilane, ammonia, borane, diborane, derivatives thereof, and combinations thereof.
 7. The method of claim 1, further comprises depositing a second nucleation layer on the first nucleation layer during a pulsed-CVD processes or an atomic layer deposition process, wherein the second nucleation layer comprises tungsten, tungsten alloys, tungsten-containing materialsm, or combinations thereof.
 8. The method of claim 7, wherein the first nucleation layer is deposited at a temperature ranging from about 400° C. to about 450° C. and maintained at a pressure ranging from about 10 Torr to about 20 Torr, and wherein the second nucleation layer is deposited at a temperature ranging from about 400° C. to about 450° C. and maintained at a pressure ranging from about 20 Torr to about 50 Torr.
 9. The method of claim 7, wherein the first nucleation layer has a thickness about 30 Å, and the second nucleation layer has a thickness in a range from about 10 Å to about 300 Å.
 10. A method for forming a tungsten-containing material on a substrate, comprising: positioning a substrate within a process chamber; exposing the substrate to a reducing gas to form a first reducing agent layer on the substrate during a pre-soak process; depositing a tungsten nitride layer over the substrate by sequentially exposing the substrate to a tungsten-containing precursor and ammonia during an atomic layer deposition process; exposing the substrate to the reducing gas to form a second reducing agent layer on the tungsten nitride layer during a second soak process; and depositing a bulk layer over the second reducing agent layer.
 11. The method of claim 10, wherein the reducing gas comprises a reducing agent selected from the group consisting of hydrogen, silane, ammonia, diborane, derivatives thereof, and combinations thereof.
 12. The method of claim 10, wherein the tungsten-containing precursor comprises tungsten hexafluoride (WF₆), tungsten hexachloride (WCl₆), tungsten carbonyl (W(CO)₆), bis(cyclopentadienyl)tungsten dichloride (Cp₂WCl₂), mesitylene tungsten tricarbonyl (C₉H₁₂W(CO)₃), or derivatives thereof.
 13. The method of claim 10, wherein the tungsten nitride layer has a thickness of about 200 Å or less.
 14. The method of claim 10, wherein the bulk layer comprises tungsten.
 15. The method of claim 14, wherein the bulk layer is deposited by a chemical vapor deposition process. 